The present study evaluated the wear resistance of three light composite resins marketed for posterior restorations. Also, the materials were compared with and without application of light and heat after initial light cure of the composite resins. Sliding-induced wear tests were conducted by sliding the specimens over the corresponding composite resin plates. Abrasive wear resistance of the materials was evaluated in tems of number of the cycles necessyto wear the specimens to a depth of 0.25 mm. The analysis of variance (ANOVA) showed statistically significant dierences between materiais with Herculite XRV composite resin showing the highest mean value (p < 0.05). In addition, when the specimens were submitted to light-heat treatment, the wear resistance of all materials was improved (p < 0.05).

Neste estudo foi avaliada a propriedade de resistência a abrasão de diferentes resinas compostas indicadas para dentes posteriores. Além disso, foi verificado o efeito da complementação fototérmica de polimenzação sobre a variável Resistência a abrasão. Para isso, foi utilizada uma máquina que realizava movimentos cíclicos de pistas de resina composta sobre as quais eram posicionados corpos-de-prova cilíndricos, confeccionados com o mesmo material. Os resultados foram obtidos em número de ciclos realizados até que ocorresse o desgaste de 0,25 mm. Os resultados foram submetidos a análise estatística indicando que a resina Herculite XRV produziu o maior valor de média de resistência a abrasão (p < 0,05). Além disso, foi verificado que a complementação fototérmica de polimerização melhorou a resistência ao desgaste das resinas avaliadas (p < 0,05).